Cynhyrchion GR4 a ddarperir gan GNEE
Gr4 Ti6AL4V ELI Gwifren Titaniwm Meddygol
Ffoil Titaniwm Gr4 Ar gyfer Diwydiannol
Cynnwys cemegol
| Cydran | Wt. % |
| C | Uchafswm 0.1 |
| Fe | Uchafswm 0.5 |
| H | Uchafswm 0.015 |
| N | Uchafswm 0.05 |
| O | Uchafswm 0.4 |
| Ti | 99 |
Ceisiadau
Cydrannau ffrâm aer, llestri cryogenig, cyfnewidwyr gwres, offer CPI, tiwbiau cyddwysydd, basgedi piclo.
Priodweddau Corfforol
| Priodweddau Corfforol | Metrig | Saesneg | Sylwadau |
| Dwysedd | 4.51 g/cc | 0.163 pwys/mewn³ |
Priodweddau Mecanyddol
| Caledwch, Brinell | 265 | 265 | annealed |
| Caledwch, Knoop | 215 | 215 | dalen heb ei weldio |
| Caledwch, Rockwell B | 100 | 100 | annealed |
| Caledwch, Rockwell B | 23 | 23 | dalen heb ei weldio |
| Caledwch, Rockwell C | 23 | 23 | Amcangyfrif o Brinell. |
| Caledwch, Vickers | 280 | 280 | Amcangyfrif o Brinell. |
| Cryfder Tynnol, Ultimate | 550 MPa | 79800 psi | |
| Cryfder Tynnol, Cynnyrch | 480 - 552 MPa | 69600 - 80100 psi | |
| Elongation at Break | 15 % | 15 % | |
| Lleihau Ardal | 30 % | 30 % | |
| Modwlws Elastigedd | 105 GPa | 15200 ksi | Mewn Tensiwn |
| Modwlws Cywasgol | 110 GPa | 16000 ksi | |
| Cryfder Gan y Pen draw | 695 MPa | 101000 psi | |
| Gan gadw Cryfder Cynnyrch | 830 MPa | 120000 psi | 2% set barhaol |
| Cymhareb Poisson | 0.37 | 0.37 | |
| Cryfder Blinder | 250 MPa | 36300 psi | ar 1E+7 gylchred. Kt(ffactor crynodiad straen)=2.7 |
| Cryfder Blinder | 290 MPa | 42100 psi | ar 100,000 o gylchoedd; Kt(ffactor crynodiad straen)=2.7 |
| Cryfder Blinder | 425 MPa | 61600 psi | 1E+7 gylchred, Heb ei nodi |
| Cryfder Blinder | 517 MPa | 75000 psi | Heb eu sgorio 100,00 o Beiciau |
| Cryfder Toriad | 99 - 140 MPa-m½ | 90.1 - 127 ksi-mewn½ | ar gyfer K(Q) wedi'i anelio |
| Modwlws cneifio | 40 GPa | 5800 ksi |
Priodweddau Trydanol
| Gwrthiant Trydanol | 6e-005 ohm-cm | 6e-005 ohm-cm |
Priodweddau Thermol
| Gwres Ymdoddiad | 325 J/g | 140 BTU/lb | Uchel Purdeb Ti. |
| CTE, llinol 20 gradd | 8.6 µm/m- gradd | 4.78 µmewn/mewn- gradd F | 0-100ºC |
| CTE, llinol 250 gradd | 9.2 µm/m- gradd | 5.11 µmewn/mewn- gradd F | Cyfartaledd dros yr ystod 0-315ºC |
| CTE, llinol 500 gradd | 9.7 µm/m- gradd | 5.39 µmewn- gradd F | 0-540ºC; Mae CTE yn berpendicwlar uwch i'r echelin c |
| Cynhwysedd Gwres Penodol | 0.53 J/g- gradd | 0.127 BTU/lb- gradd F | gwerth ar 540ºC yw 0.67 J/g-ºC |
| Dargludedd Thermol | 17.2 W/m-K | 119 BTU-mewn/awr-ft²- gradd F | |
| Ymdoddbwynt | 1660 gradd ar y mwyaf | Uchafswm o 3020 gradd F | Hylif |
| Hylif | 1660 gradd | 3020 gradd F | |
| Beta Transus | 950 gradd | 1740 gradd F |
Cynhyrchion titaniwm a ddarperir gan GNEE
|
Safonol
|
ASTM B338/ASME SB338, ASTM B337/ASME SB337, ASTM B861/ASME SB{5}}, ASTM B862/ASME SB862, AMS4911,AMS4928
|
|
Gradd Deunydd
|
Gr1, Gr2, Gr4, Gr7, Gr9, Gr11, Gr12, ac ati
|
|
Hyd
|
Llai na neu'n hafal i 15000mm
|
|
Maint(mm)
|
Diamedr 3-114mm
|
|
Siâp adran
|
Rownd / Sgwâr
|
|
Goddefgarwch |
a) Diamedr Allanol: +/- 0.01mm
|
|
b) Trwch: +/- 0.01mm
|
|
|
c) Hyd: +/- 0.1mm
|
|
|
Arwyneb
|
Piclo, anelio, caboli, llachar.
|
|
Nodwedd
|
Dwysedd 1.Low a Chryfder Uchel
2.Excellent Corydiad Resistance Gwrthwynebiad 3.Good i effaith gwres 4.Excellent Gan gadw i eiddo cryogenig 5.Anmagnetig ac An-wenwynig Priodweddau thermol 6.Good Modwlws 7.Low o Elastigedd |
|
Prawf
|
Prawf sboncen, prawf estynedig, prawf pwysedd dŵr, prawf pydredd grisial, triniaeth wres, NDT
|
|
Deunydd
|
Titaniwm pur ac aloi Titaniwm
|
|
Gradd Titaniwm
|
GR1/GR2/GR3/Gr4/GR5/GR7/GR9/GR12/Gr5Eli/Gr23
|
|
Safonol
|
ASTM B348/ASME SB348, ASTMF67, ASTM F136, ISO-5832-2(3), AMS 4928 ac ati
|
|
Siâp
|
Gwialen / bar crwn titaniwm, gwialen / bar sgwâr Titaniwm, gwialen / bar fflat Titaniwm
Gwialen / bar petryal titaniwm, gwialen / bar hecs Titaniwm |
|
Diamedr
|
1-300mm, y gellir ei addasu
|
|
Hyd
|
50mm-6000mm, yn addasadwy
|
|
Goddefgarwch
|
h6~h13 H10~H13
|
|
Arwyneb
|
Disglair/Caboledig/Peiriannu
|
|
Prif Dechneg
|
Gofannu Poeth; Rholio Poeth; Wedi'i dynnu'n oer; Sythu etc
|
|
Triniaeth Gwres
|
Fel arfer yn cael eu Annealled, ond Solid Ateb a Heneiddio gall fod yn iawn hefyd
|
|
Tystysgrif Melino Deunydd
|
Yn ôl. EN 10204.3.1
Gan gynnwys Cyfansoddiad cemegol ac eiddo Mecanyddol |
|
Cais
|
Meteleg, Electroneg, Meddygol, Cemegol, Petrolewm, Fferyllol, awyrofod, ac ati.
|
plât titaniwm / taflen / stribed
|
Safonol |
ASTM B265 JIS H4600 GB/T 3620.1 |
|
Gradd |
ASTM Ti Pur: Gr.1 Gr.2 Gr.3 Gr.4 Ti Alloy: Gr.5 Gr.7 Gr.9 Gr.11JIS Pur Ti: Dosbarth 1 Dosbarth 2 Dosbarth 3 Dosbarth 4;Ti Alloy: Dosbarth 60 |
|
Maint |
trwch 0.3mm ~ 100mm; Lled 50mm ~ 2500mm; Hyd 1000mm ~ 12000mm |
|
Arwyneb |
Gorffeniad melin, caboledig, anodizing, brwsio, ffrwydro tywod, cotio powdr, ac ati |
|
Cais |
1) Teclyn gwneud pellach. |
|
Gradd |
GR1, GR2, GR3, GR4, GR5, GR7, GR9, GR11, GR12, GR23 ac ati. ERTi-1, ERTi-2, ERTi-3, ERTi-4, ERTi-5, ERTi-7, ERTi-9, ERTi-11, ERTi-12 |
|
Maint |
Dia: 0.1-8mm neu gellir ei addasu |
|
Safonol |
ASTM B348, ASME SB348, ASTM B863, AWS.A5.16, GB/T3623-2007 |
|
MOQ |
10kg |
|
Ansawdd a phrawf |
Anelio, profion uwchsonig |
|
Cais |
Awyrofod, Cemegol, Meddygol, Fframiau Llygaid, Weldio ac ati |
|
Nodwedd |
Cryfder uchel, Pwysau ysgafn, Dargludiad gwres ardderchog a gwrthsefyll cyrydiad |
|
Cyflwr |
Annealed (M), Gwaith Poeth (R), Oer Gweithio (Y) |
|
Arwyneb |
Llachar, caboledig, piclo, sgwrio â thywod |
|
Pecyn |
Blwch Pren |